dc.description.abstractTelah dilakukan penelitian tentang betonpolimer dari campuran bahan pasir, serbuk cangkang telur, serat tebu serta resin epoksi sebagai matriks. Penelitian ini bertujuan untuk mengetahui pengaruh penambahan serbuk cangkang telur dan serat tebu terhadap sifat fisis dan mekanik dari beton polimer. Beton polimer ini dibuat dengan perbandingan yaitu komposisi pasir : serbuk telur : serat tebu (50:50:0), (50:49:1), (50:48:2), (50:47:3), (50:46:4) dan (50:45:5) dalam satuan gram. Dan resin epoksi sebagai perekat dibuat (20,25,30)% dari berat total pasir, serbuk telur dan serat tebu. Preparasi benda uji dilakukan dengan tahapan sebagai berikut: penimbangan, pencampuran, pencentakan dengan hotpress selama 20 menit dengan suhu 90˚C. parameter yang diuji antara laini: uji fisis (densitas, porositas, dan penyerapan air), uji mekanik (kuat lentur, kuat tekan dan kuat tarik) serta uji mikrostruktur dengan SEM. Dari hasil pengamatan diperoleh komposisi optimum untuk uji fisis (densitas 1,76 gr/m3, porositas 1,897 % dan penyerapan air 1,078 %) sedangkan komposisi optimum untuk uji mekanik (kuat lentur 18,39 MPa, kuat tekan 26,27 MPa, dan kuat tarik 4,02 MPa). Mikrostuktur beton polimer dianalisa dengan menggunakan SEM menunjukkan bahwa sampel denganresin 20% lebih merata dan mengikat bahan.en_US
dc.description.abstractResearch has been carried out on polymer concrete from a mixture of sand, eggshell powder, baggase and epoxy resin as a matrix. The research aims to knowing the effect of adding eggshell powder and baggase to the physical properties and mechanical properties of polymer concrete. This polymer concrete is made by comparison of composition of sand : eggshell powder : baggase (50:50:0), (50:49:1), (50:48:2), (50:47:3), (50:46:4) and (50:45:5) in grams. And epoxy resin as a matrix made (20,25,30)% of the total weight of sand, eggshell powder and baggase. Preparation of the test object is carried out with the following stages: weighing, mixing, printing with hotpress for 20 minutes at a temperature of 90˚C. the parameters tested were: physical test (density, porosity, and water absorption), mechanical tests (flexural strength, comperesive strength and tensile strength) and microstructure analysis with SEM. From the observations obtained the optimum composition for the physical test (density 1.76 gr / m3, porosity 1.897% and water absorption 1.078%) while the optimum composition for mechanical tests (flexural strength 18.39 MPa, compressive strength of 26.27 MPa, and strong pull 4.02 MPa). Microstructure of polymer concrete analized using SEM showed that samples with 20% epoxy resin werw more evenly distributed in binding materials.en_US
dc.language.isoiden_US
dc.publisherUniversitas Sumatera Utaraen_US
dc.subjectBeton Polimeren_US
dc.subjectResin Epoksien_US
dc.subjectSerat Tebuen_US
dc.subjectSerbuk Cangkang Teluren_US
dc.titleKarakterisasi Beton Polimer dengan Campuran Serbuk Cangkang Telur dan Serat Tebuen_US
dc.typeSkripsi Sarjanaen_US
dc.identifier.nimnipnik150801033