dc.description.abstractDalam penelitian ini, penambahan PEO (Polietilen Oksida) pada larutan kitosan telah berhasil meningkatkan sifat elektrik dan penginderaan film kitosan sebagai sensor kelembaban udara berdasarkan hasil-hasil pengujian. Variasi konsentrasi penambahan PEO pada larutan kitosan yaitu 0,1%; 0,2%; 0,3%; 0,4% dan 0,5% (w/v). Sensor difabrikasi dalam bentuk film menggunakan metode solution casting. Pengujian kelembaban udara dilakukan dengan menempatkan film di dalam mesin pendingin model KT-2000 Ahu. Hasil pengujian menunjukkan penambahan PEO pada film kitosan menghasilkan peningkatan konduktivitas listrik sebesar 41,25%; 80,00%; 122,50%; 85,00% dan 48,75% untuk penambahan PEO dengan konsentrasi 0,1; 0,2; 0,3; 0,4 dan 0,5% secara berturut-turut. Selain itu, pengujian respon pada sifat penginderaan film kitosan dengan penambahan PEO meningkatkan tegangan keluaran, dibandingkan dengan kitosan murni yaitu diatas 300 mV sedangkan kitosan murni dibawah 300 mV. Di antara variasi PEO, tegangan keluaran maksimum dari PEO 0,3% adalah diatas 400 mV. Sedangkan tegangan keluaran maksimum dari konsentrasi PEO yang lain dibawah 400 mV. Selain itu, sensor film kitosan dengan penambahan PEO 0,3% menunjukkan sensitivitas yang paling tinggi sebesar 5,34 serta memiliki perulangan dan stabilitas yang baik. Oleh karena itu, sensor film kitosan dengan konsentrasi penambahan PEO 0,3% menunjukkan sifat elektrik dan penginderaan yang baik pada film kitosan untuk diaplikasikan sebagai sensor kelelmbaban udara.en_US
dc.description.abstractIn this study, the addition of PEO (Polyethylene Oxide) in chitosan solution has successfully improved the electrical and sensing properties of chitosan film as humidity sensor based on measurement results. The concentration variety of PEO in chitosan solution is 0,1%; 0,2%; 0,3%; 0,4% and 0,5% (w/v). The sensors were fabricated in film form using a solution casting method. The humidity testing was perfomed by placing a film in the cooling machine room, model KT-2000 Ahu. The measurement results showed that the addition of PEO in chitosan films increased the electrical conductivity of 41,25%; 80,00%; 122,50%; 85,00% and 48,75% by adding the PEO which has concentrations of 0,0; 0,1; 0,2; 0,3; 0,4 and 0,5 % respectively. In addition, the response in sensing properties by adding the PEO increased the output voltage than the pure chitosan which was above 300 mV while the pure chitosan was under 300 mV. Among the variations in PEO, the maximum output voltage of 0,3% PEO is above 400 mV. Meanwhile, the maximum output voltage of other PEO concentrations was 400 mV. Moreover, the chitosan film sensor by adding the 0,3% of PEO showed the highest sensitivity of 5,34 and has a good repeatibility and stability. Therefore, chitosan film sensors by adding the 0,3% of PEO showed good electrical and sensing properties of chitosan films to be applied as humidity sensor.en_US
dc.language.isoiden_US
dc.publisherUniversitas Sumatera Utaraen_US
dc.subjectKelembaban Udaraen_US
dc.subjectKitosanen_US
dc.subjectSensoren_US
dc.subjectPolietilen Oksidaen_US
dc.titlePeningkatan Sifat Elektrik dan Penginderaan Film Kitosan dengan Penambahan Peo (Polietilen Oksida) Sebagai Sensor Kelembaban Udaraen_US
dc.typeSkripsi Sarjanaen_US
dc.identifier.nimnipnik150801055


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record