Pembuatan dan Karakterisasi Beton Polimer dengan Agregat Batu Apung Serta Serat Daun Singkut Sebagai Filler

Abstract

Reseach has bee conducted on the manufacture and characteriation of polymer based on concrete sand, pumice, singkut leaf fibers and epoxy resin with a variety of composition. Singkut leaf fibers are soaked in 5% and 13% NaOH solution and mixed with sand, floating stone, and epoxy resin with a certain composition. The mixture is printed with a hot press at 90°C for 20 minutes. The characterization results show that the best composition is A2 consisting of sand:pumice:singkut leaf fiber:epoxy resin (60:18:2:20) gr with a density value of 1,74 gr/cm3, porosity of 0,6%, water absorption of 0,34%, flexural strength of 37,07 MPa, compressive strength of 60,18 MPa,tensile strength of 8,33 MPa. Microstructure test results show that polymer concrete samples are dominated by element C (Carbon).

Telah dilakukan penelitian tentang pembuatan dan karakterisasi beton polimer berbasis pasir, batu apung, serat daun singkut dan resin epoksi dengan berbagai variasi komposisi. Serat daun singkut di rendam dalam larutan NaOH 5% dan 13% dan dicampur dengan pasir,batu apung, dan resin epoksi dengan komposisi tertentu. Campuran tersebut di cetak dengan hot press pada suhu 90°C selama 20 menit. Hasil karakterisasi menunjukkan bahwa komposisi terbaik adalah A2 yang terdiri dari pasir:batu apung: serat daun singkut: resin epoksi (60:18:2:20) gr dengan nilai densitas sebesar 1,74 gr/cm3, porositas sebesar 0,6%, penyerapan air sebesar 0,34%, kuat lentur sebesar 37,07 MPa, kuat tekan sebesar 60,18 MPa, kuat tarik sebesar 8,33 MPa. Hasil pengujian mikrostruktur menunjukkan bahwa sampel beton polimer didominasi oleh unsur C (Karbon).