Pemanfataan Limbah Cair Kelapa Sawit (Sludge) untuk Pembuatan Batako

Abstract

Palm oil liquid waste is extraction results from palm oil processing, a research has been carried out to utilize sludge’s liquid waste for the production of concrete brick from sand mixture, portland cement, water and palm oil sludge waste as an alternative material. The result of this research are the concrete brick in size 10x2x1 cm with drying process by using sunlight for 14 days has good physical properties but there is decrease in the value of mechanical properties. The optimum value of physical properties obtained after the addition of sludge is 2,18 gr/cm for density, 40% for porocity, 29,62 % for water absorption. While the optimum value of mechanical properties obtained is 6,94 Mpa for compressive strength, and 3624 J/m2 for strong impact. And for microstructure analysis by using XRD

Limbah cair kepala sawit merupakan hasil ekstraksi minyak dari proses pengolahan kelapa sawit. Maka telah dilakukan penelitian untuk memanfaatkan limbah cair sludge tersebut untuk pembuatan batako dari bahan campuran pasir, semen portland, air dan limbah sludge kelapa sawit sebagai alternatif bahan material. Hasil penelitian ini adalah bahwa batako dengan ukuran 10x2x1 cm dengan proses pengeringan pada sinar matahari selama 14 hari memiliki sifat fisis yang baik namun ada penurunan nilai pada sifat mekanik. Nilai optimum sifat fisis yang didapat setelah penambahan sludge adalah 2,18 gr/cm3 untuk densitas, 40% untuk porositas, 29,62% untuk penyerapan air. Sedangkan nilai optimum sifat mekanik yang didapat adalah 6,94 MPa untuk kuat tekan dan 3624 J/m2 untuk kuat impak. Serta untuk analasisa mikrostrukturnya menggunakan XRD.