Pemanfaatan Limbah Plastik Polipropilena dan Serbuk Batang Kelapa Sawit sebagai Bahan Isolasi Listrik

Abstract

The utilization of polypropylene plastic wastes and oil palm wood has been investigated for producing electrical isolation material. In this work combination of polypropylene plastic ( PP) waste and oil palm wood ( OPW ) powder has been carried out to produce isolation material. Results showed that the combination can be used for isolation material were based on their characteristic. The combination of OPW 50 % is 50 % PP dielectrical strength of the material was higher than that of air at 25ºC and 1 atmospheric pressure. The resistance of the material with combination 40 % PP and 60 % OPW was 1,14 x 1010 ?.cm which was similar to that of cellulose material.This work can be affered as alternatif for eliminating PP wastes and the application of OPW wastes.

Pemanfatan limbah plastik polipropilena dengan limbah serbuk batang kelapa sawit telah diteliti untuk pembuatan bahan isolasi listrik. Dalam penelitian ini dilakukan penggabungan antara limbah plastik polipropilena dengan serbuk batang kelapa sawit dijadikan bahan isolasi listrik. Hasil dari penelitian ini menunjukan bahwa kombinasi ini dapat dipergunakan sebagai bahan isolosi listrik sesuai dengan karakteristik bahan isolasi itu sendiri. Pada komposisi 50 % Polipropilena dan 50 % serbuk KKS mempunyai nilai kekuatan dielektrik diatas kekuatan dielektrik udara pada suhu 25 ºC dengan tekanan 1 atm dan mempunyai nilai tahanan jenis 1010?.cm dengan kornposisi 40 % polipropilena dan 60 % serbuk KKS dimana nilai ini sudah menyamai nilai tahanan jenis selulosa. Hasil penelitian ini dapat ditawarkan sebagai alternatif untuk mengurangi limbah plastik polipropilena dan sekaligus pemanfaatan serbuk batang kelapa sawit.