Pembuatan Keramik Paduan Cordierit-Alumina sebagai Bahan Refraktori dan Karakterisasinya

Abstract

Cordierit ceramic (2MgO.2Al2O3.5SiO2) making has already been brought in by employing local stuffs through. Such stuffs which are employed ini order to gain cordierit powder consist of sand of silica as the source of SiO3, magnesit (MgCO3) as the source of MgO and technical alumina as the supplier of Al2O3. From the yield cordierit- alumina ceramic gained, we can characterize porosity, density, termal expancy coefficient test, endurance and microstructure analysis by using XRD and SEM.The DTA analysis result show that cordierit begins to be gained on 12400C by which the temperature of calcinacy should be 12500C.

Telah dilakukan pembuatan Keramik paduan Cordierit 2MgO.2Al2O3.5SiO2- Alumina (Al2O3) dengan menggunakan bahan baku lokal melalui reaksi padatan. Bahan baku yang digunakan untuk mendapatkan serbuk Cordierit adalah pasir silika sebagai sumber SiO3, magnesit (MgCO3) sebagai sumber MgO dan alumina teknis sebagai sumber AL2O3. Dari hasil pembuatan keramik paduan Cordierit - Alumina maka dilakukan karakterisasi meliputi Porositas, Densitas, Pengujian Koefisien Ekspansi Termal, Kuat Patah dan Analisa Mikro Struktur dengan menggunakan XRD dan SEM.Hasil analisa Differential Thermal Analysis (DTA) menunjukkan bahwa Cordierit mulai terbentuk pada suhu 12400C, sehingga suhu kalsinasi dipilih 12500C.