Pembuatan Membran Kitin dan Pengujian Sifat Permeabilitasnya terhadap Ureum, Aspirin dan Albumin

Abstract

Chitin Membrane can be prepared by dissolving chitin in mixed solvent trichloro acetic acid-dichloromethane 40 %. In order to obtain a good membrane, concentration of chitin was 0.6 - 0.8 %, and the solvent used for immersion was 2-propanol, followed with cold water and hot water so that the transparent membrane will be produced on thin plate of glass. Drying process of membrane was conducted at room temperature. The membrane was than examined its permeability behavior against ureum, aspirin and albumin having different molecular weight and the result showed that the albumin did not diffuse through the membrane while ureum and aspirin did. By comparing permeability properties of chitin membrane and cellulose acetate one (cellophane) it was shown that both permeation characteristics of membranes were same against ureum, aspirin and albumin.

Membran kitin dapat dibuat dengan melarutkan kitin dalam campuran pelarut asam trikloro asetat-dikorometan 40 %. Untuk menghasilkan membran yang baik, konsentrasi kitin adalah 0,6 - 0,8 % dan pelarut untuk immersi adalah 2-propanol kemudian di imersikan kembali dengan air dingin dan air panas sehingga diperoleh membran yang transparan pada permukaan plat kaca, Proses pengeringan membran dilakukan pada suhu kamar, Membran yang dihasilkan diuji sifat permeabiIitasnya terhadap urea aspirin dan albumin yang mempunyai berat molekul berbeda-beda dan hasil yang diperoleh menunjukkan bahwa albumin tidak dapat terdiffusi melewati membrane sedangkan urea dan aspirin dapat terdiffusi. Dengan membandingkan sifat pemeabilitas membran kitin dengan membran sellulosa asetat (Cellophane) diperoleh bahwa karakteristik permeasi membran tersebut adalah sarna terhadap urea, aspirin dan albumin.