Pengaruh Zat Aktif Pemutih Gigi terhadap Kekuatan Geser Perlekatan Breket Logam (Penelitian Laboratoris)

Abstract

Adhesion of orthodontic bracket based on mechanical bonding between adhesive agent and the adhesion. Bracket adhesion is influenced by the enamel condition, base form of the bracket and the bonding agent. The objective of the study in vitro is to acknowledge the effect of dental bleaching additive agent of 38% hydrogen peroxide and 35% carbamid peroxide and the effect of interval of attaching the post-bleaching bracket on the shear bond strength of the bracket bonding. Eighty extracted human upper premolars were cleaned and submerged into saline solution. The samples were divided randomly into 8 groups. The group A1 B1 subjected to bleached by hydrogen peroxide, bracket attachment and debonding were conducted 1 day post- bleaching, the A1 B2 was bleached by the hydrogen peroxide, the bracket attachment and debonding were conducted 15 days-post bleaching, the A1 B3 was bleached by hydrogen peroxide , bracket attachment and debonding were conducted 30 days-post bleaching, the A2 B1 was bleached by carbamid peroxide, the bracket attachment and debonding were conducted 1 day post-bleaching, the A2 B2 was bleached by carbamid peroxide, the bracket attachment and debonding were conducted 15 days post-bleaching, the A2 B2 was bleached by carbamid peroxide, the bracket attachment and debonding were conducted 30 days-post bleaching, control group and the group without etching were prior to the bracket attachment. ANOVA test showed the significant difference of shear bond strength of bracket adhesion between control and group bleached by both hydrogen peroxide and carbamid peroxide (p0.05). There was a significant effect in interval of metal bracket attachment between one day and after 15 days and 30 days post bleaching using both 38% hydrogen peroxide and 35% carbamid peroxide on the shear bond strength of metal bracket attachment (p<0.05).

Perlekatan breket ortodonti berdasarkan pada suatu penguncian mekanikal antara bahan perekat dan perlekatannya. Perlekatan breket dipengaruhi oleh keadaan enamel, bentuk basis breket dan bahan bonding. Tujuan penelitian in vitro ini adalah untuk mengetahui pengaruh zat aktif pemutih gigi hidrogen peroksida 38% dan karbamid peroksida 35% serta pengaruh interval waktu pemasangan breket postbleaching terhadap kekuatan geser perlekatan breket. Sebanyak 80 gigi premolar atas yang telah dicabut, dibersihkan, dan direndam dalam larutan salin. Sampel dibagi secara acak kedalam 8 kelompok. Kelompok A1 B1 dilakukan bleaching dengan hidrogen peroksida, pemasangan breket dan debonding dilakukan setelah 1 hari postbleaching, A1 B2 bleaching dengan hidrogen peroksida pemasangan breket dan debonding dilakukan setelah 15 hari postbleaching, A1 B3 bleaching dengan hidrogen peroksida pemasangan breket dan debonding dilakukan 30 hari setelah postbleaching, A2 B1 bleaching dengan karbamid peroksida pemasangan breket dan debonding dilakukan setelah 1 hari postbleaching, A2 B2 bleaching dengan karbamid peroksida, pemasangan breket dan debonding dilakukan setelah 15 hari postbleaching, A2 B3 bleaching dengan karbamid peroksida pemasangan breket dan debonding dilakukan 30 hari setelah postbleaching, kelompok kontrol serta kelompok tanpa etching sebelum pemasangan breket. Uji ANOVA menunjukkan adanya perbedaan yang signifikan kekuatan geser perlekatan breket antara kelompok kontrol dengan kelompok yang dilakukan bleaching hidrogen peroksida maupun karbamid peroksida (p<0.05). Tidak ada perbedaan yang signifikan kekuatan geser perlekatan breket antara kelompok yang dibleaching dengan hidrogen peroksida dengan karbamid peroksida (p>0.05). Ada perbedaan yang bermakna pada interval waktu pemasangan breket logam antara satu hari dan setelah 15 hari dan 30 hari postbleaching dengan menggunakan hidrogen peroksida 38% dan karbamid peroksida 35% terhadap kekuatan geser perlekatan breket logam (p<0.05).