Pengaruh Perbandingan Asam Oleat sebagai Template dengan Tetraetilortosilikat (TEOS) sebagai Sumber Silika Terhadap Porositas Material Mesopori Silika

Abstract

Mesoporous silica material has been synthesized using tetraethylortosilicate (TEOS) as a source of silica, oleic acid as template and 3-aminopropyltrimethoxysilane (APMS) as co-structure directing agents (CSDA). The synthesis of material silica was made with variation mol of TEOS : Oleic Acid with a ratio of 1: 0.2; 1: 0.3; 1: 0.5; 1: 0.6; 1: 0.7; 1: 0.9 and 1: 1. The product XRD analysis has a wide diffraction peak that indicates an amorphous material. The FT-IR spectrum shows the Si-OH and Si-O-Si groups which are characteristic of silica material. SEM photographs show the presence of pores on a slit-shaped silica material (plate). Adsorption desorption isotherm (BET) shows an isotherm type IV curve and the dominant pore size are 1,945 and 4,588 nm.

Telah dilakukan sintesis material mesopori silika dengan menggunakan tetraetilortosilikat (TEOS) sebagai sumber silika, asam oleat sebagai template dan 3-aminopropiltrimetoksisilana (APMS) sebagai co-structure directing agents (CSDA). Sintesis material silika dibuat dengan variasi TEOS : Asam Oleat menggunakan satuan mol dengan perbandingan 1 : 0,2 ; 1 : 0,3 ; 1 : 0,5 ; 1 : 0,6 ; 1 : 0,7 ; 1 : 0,9 dan 1 : 1 . Hasil analisa XRD produk memiliki puncak difraksi yang melebar yang menunjukkan material bersifat amorf. Spektrum FT-IR memiliki gugus Si-OH dan Si-O-Si yang merupakan karakteristik material silika. Foto SEM menunjukkan adanya pori pada material silika yang berbentuk celah (plat). Adsorpsi desorpsi isotherm (BET) menunjukkan kurva isotherm tipe IV dan ukuran pori dominan adalah 1,945 dan 4,588 nm.